Evaluation of residual stresses in the bulk of materials by high energy synchrotron diffraction

Journal Article


Abstract


  • High energy synchrotron diffraction is introduced as a new method for residual stress analysis in the bulk of materials. It is shown that energy dispersive measurements are sufficiently precise so that strains as small 10-4 can be determined reliably. Due to the high intensity and the high parallelism of the high energy synchrotron radiation the sample gauge volume can be reduced to approximately 50 mμ × 1 mm × 1 mm compared to gauge volume of one mm3 up to several mm3 achievable by neutron diffraction. The benefits of the high penetration depth and the small gauge volume are demonstrated by the results of stress studies performed on a fiber reinforced ceramic, a functional gradient material and a metal-ceramic compound. Furthermore, it is shown that in case of a cold extruded metal specimen the energy dispersive measurement technique yields simultaneous information about texture and residual stresses and thus allows a detailed investigation of elastic and plastic deformation gradients. © 1998 Plenum Publishing Corporation.

Publication Date


  • 1998

Citation


  • Reimers, W., Broda, M., Brusch, G., Dantz, D., Liss, K. D., Pyzalla, A., . . . Tschentscher, T. (1998). Evaluation of residual stresses in the bulk of materials by high energy synchrotron diffraction. Journal of Nondestructive Evaluation, 17(3), 129-140. doi:10.1023/A:1022607030355

Scopus Eid


  • 2-s2.0-0032157869

Start Page


  • 129

End Page


  • 140

Volume


  • 17

Issue


  • 3

Abstract


  • High energy synchrotron diffraction is introduced as a new method for residual stress analysis in the bulk of materials. It is shown that energy dispersive measurements are sufficiently precise so that strains as small 10-4 can be determined reliably. Due to the high intensity and the high parallelism of the high energy synchrotron radiation the sample gauge volume can be reduced to approximately 50 mμ × 1 mm × 1 mm compared to gauge volume of one mm3 up to several mm3 achievable by neutron diffraction. The benefits of the high penetration depth and the small gauge volume are demonstrated by the results of stress studies performed on a fiber reinforced ceramic, a functional gradient material and a metal-ceramic compound. Furthermore, it is shown that in case of a cold extruded metal specimen the energy dispersive measurement technique yields simultaneous information about texture and residual stresses and thus allows a detailed investigation of elastic and plastic deformation gradients. © 1998 Plenum Publishing Corporation.

Publication Date


  • 1998

Citation


  • Reimers, W., Broda, M., Brusch, G., Dantz, D., Liss, K. D., Pyzalla, A., . . . Tschentscher, T. (1998). Evaluation of residual stresses in the bulk of materials by high energy synchrotron diffraction. Journal of Nondestructive Evaluation, 17(3), 129-140. doi:10.1023/A:1022607030355

Scopus Eid


  • 2-s2.0-0032157869

Start Page


  • 129

End Page


  • 140

Volume


  • 17

Issue


  • 3