Texture and boundary characteristics of severely deformed and recrystallized copper

Conference Paper


Abstract


  • Oxygen-free high conductivity copper was subjected to room temperature equal channel angular extrusion of 8 passes using route Bc. The resulting ultra-fine grain copper was then rolled to thickness reductions of up to 96.5% at liquid nitrogen temperatures. Annealed coarse grained copper was rolled to the same strain at room temperature for comparison. Samples from the two routes were isochronally and isothermally annealed, and the microstructure and texture evolution studied by electron back scattered diffraction and x-ray diffraction. Annealing of the ultrafine grained copper led to the development of a strong rotated cube texture from a texture in the rolled material dominated by the Brass component. In contrast the more commonly observed cube texture was found after annealing of the coarse-grained sample. Accompanying the rotated cube texture was the development of a large fraction of boundaries with rotation angle/axis close to 60° 〈111〉.

Publication Date


  • 2007

Citation


  • Davies, C. H. J., Cao, W. Q., Gu, C. F., Lapovok, R. Y., & Pereloma, E. V. (2007). Texture and boundary characteristics of severely deformed and recrystallized copper. In Materials Science Forum Vol. 558-559 (pp. 177-182). doi:10.4028/0-87849-443-x.177

Scopus Eid


  • 2-s2.0-38349152844

Web Of Science Accession Number


Start Page


  • 177

End Page


  • 182

Volume


  • 558-559

Issue


  • PART 1

Abstract


  • Oxygen-free high conductivity copper was subjected to room temperature equal channel angular extrusion of 8 passes using route Bc. The resulting ultra-fine grain copper was then rolled to thickness reductions of up to 96.5% at liquid nitrogen temperatures. Annealed coarse grained copper was rolled to the same strain at room temperature for comparison. Samples from the two routes were isochronally and isothermally annealed, and the microstructure and texture evolution studied by electron back scattered diffraction and x-ray diffraction. Annealing of the ultrafine grained copper led to the development of a strong rotated cube texture from a texture in the rolled material dominated by the Brass component. In contrast the more commonly observed cube texture was found after annealing of the coarse-grained sample. Accompanying the rotated cube texture was the development of a large fraction of boundaries with rotation angle/axis close to 60° 〈111〉.

Publication Date


  • 2007

Citation


  • Davies, C. H. J., Cao, W. Q., Gu, C. F., Lapovok, R. Y., & Pereloma, E. V. (2007). Texture and boundary characteristics of severely deformed and recrystallized copper. In Materials Science Forum Vol. 558-559 (pp. 177-182). doi:10.4028/0-87849-443-x.177

Scopus Eid


  • 2-s2.0-38349152844

Web Of Science Accession Number


Start Page


  • 177

End Page


  • 182

Volume


  • 558-559

Issue


  • PART 1