Effects of aluminum and titanium on the microstructure of ODS steels fabricated by hot pressing

Journal Article


Abstract


  • Three oxide-dispersion-strengthened (ODS) steels with compositions of Fe���14Cr���2W���0.2V���0.07Ta���0.3Y2O3 (wt%, so as the follows) (14Y), Fe���14Cr���2W���0.2V���0.07Ta���1Al���0.3Y2O3 (14YAl), and Fe���14Cr���2W���0.2V���0.07Ta���0.3Ti���0.3 Y2O3 (14YTi) were fabricated by hot pressing. Transmission electron microscopy (TEM) was used to characterize the microstructures and nanoparticles of these ODS steels. According to the TEM results, 14Y, 14YAl, and 14YTi ODS steels present similar bimodal structures containing both large and small grains. The addition of Al or Ti has no obvious effect on the microstructure of the steels. The spatial and size distribution of the nanoparticles was also analyzed. The results indicate that the average size of nanoparticles in the 14YTi ODS steel is smaller than that in the 14YAl ODS steel. Nanoparticles such as Y2O3, Y3Al5O12 and YAlO3, and Y2Ti2O7 were identified in the 14Y, 14YAl, and 14YTi ODS steels, respectively.

Publication Date


  • 2018

Citation


  • Zhao, Q., Yu, L. M., Liu, Y. C., Huang, Y., Ma, Z. Q., & Li, H. J. (2018). Effects of aluminum and titanium on the microstructure of ODS steels fabricated by hot pressing. International Journal of Minerals, Metallurgy and Materials, 25(10), 1156-1165. doi:10.1007/s12613-018-1667-7

Scopus Eid


  • 2-s2.0-85054150130

Start Page


  • 1156

End Page


  • 1165

Volume


  • 25

Issue


  • 10

Place Of Publication


Abstract


  • Three oxide-dispersion-strengthened (ODS) steels with compositions of Fe���14Cr���2W���0.2V���0.07Ta���0.3Y2O3 (wt%, so as the follows) (14Y), Fe���14Cr���2W���0.2V���0.07Ta���1Al���0.3Y2O3 (14YAl), and Fe���14Cr���2W���0.2V���0.07Ta���0.3Ti���0.3 Y2O3 (14YTi) were fabricated by hot pressing. Transmission electron microscopy (TEM) was used to characterize the microstructures and nanoparticles of these ODS steels. According to the TEM results, 14Y, 14YAl, and 14YTi ODS steels present similar bimodal structures containing both large and small grains. The addition of Al or Ti has no obvious effect on the microstructure of the steels. The spatial and size distribution of the nanoparticles was also analyzed. The results indicate that the average size of nanoparticles in the 14YTi ODS steel is smaller than that in the 14YAl ODS steel. Nanoparticles such as Y2O3, Y3Al5O12 and YAlO3, and Y2Ti2O7 were identified in the 14Y, 14YAl, and 14YTi ODS steels, respectively.

Publication Date


  • 2018

Citation


  • Zhao, Q., Yu, L. M., Liu, Y. C., Huang, Y., Ma, Z. Q., & Li, H. J. (2018). Effects of aluminum and titanium on the microstructure of ODS steels fabricated by hot pressing. International Journal of Minerals, Metallurgy and Materials, 25(10), 1156-1165. doi:10.1007/s12613-018-1667-7

Scopus Eid


  • 2-s2.0-85054150130

Start Page


  • 1156

End Page


  • 1165

Volume


  • 25

Issue


  • 10

Place Of Publication