Complete set of material constants of Pb (In1/2Nb1/2) O3 -Pb (Mg1/3 Nb2/3) O3 - PbTiO3 single crystal with morphotropic phase boundary composition

Journal Article


Abstract


  • Using combined resonance and ultrasonic methods, a full set of material constants has been measured for morphotropic phase boundary (MPB) composition xPb (In1/2 Nb1/2) O3 - (1-x-y) Pb (Mg 1/3 Nb2/3) O3 -y PbTiO3 (PIN-PMN-PT) single crystals poled along [001] c. Compared with the MPB composition (1-x) Pb (Mg1/3 Nb2/3) O3 -x PbTiO3 (PMN-PT) single crystals, the PIN-PMN-PT single crystals have smaller anisotropy, higher Curie temperature (Tc ���197 ��C), and higher rhombohedral to tetragonal phase transition temperature (TR-T ���96 ��C). The electromechanical properties obtained here are the best found so far for this ternary system with d33 ���2742 pC/N, d31 ���-1337 pC/N, k33 ���95%, and k31 ���65%. �� 2009 American Institute of Physics.

Publication Date


  • 2009

Citation


  • Liu, X., Zhang, S., Luo, J., Shrout, T. R., & Cao, W. (2009). Complete set of material constants of Pb (In1/2Nb1/2) O3 -Pb (Mg1/3 Nb2/3) O3 - PbTiO3 single crystal with morphotropic phase boundary composition. Journal of Applied Physics, 106(7). doi:10.1063/1.3243169

Scopus Eid


  • 2-s2.0-70350092525

Volume


  • 106

Issue


  • 7

Place Of Publication


Abstract


  • Using combined resonance and ultrasonic methods, a full set of material constants has been measured for morphotropic phase boundary (MPB) composition xPb (In1/2 Nb1/2) O3 - (1-x-y) Pb (Mg 1/3 Nb2/3) O3 -y PbTiO3 (PIN-PMN-PT) single crystals poled along [001] c. Compared with the MPB composition (1-x) Pb (Mg1/3 Nb2/3) O3 -x PbTiO3 (PMN-PT) single crystals, the PIN-PMN-PT single crystals have smaller anisotropy, higher Curie temperature (Tc ���197 ��C), and higher rhombohedral to tetragonal phase transition temperature (TR-T ���96 ��C). The electromechanical properties obtained here are the best found so far for this ternary system with d33 ���2742 pC/N, d31 ���-1337 pC/N, k33 ���95%, and k31 ���65%. �� 2009 American Institute of Physics.

Publication Date


  • 2009

Citation


  • Liu, X., Zhang, S., Luo, J., Shrout, T. R., & Cao, W. (2009). Complete set of material constants of Pb (In1/2Nb1/2) O3 -Pb (Mg1/3 Nb2/3) O3 - PbTiO3 single crystal with morphotropic phase boundary composition. Journal of Applied Physics, 106(7). doi:10.1063/1.3243169

Scopus Eid


  • 2-s2.0-70350092525

Volume


  • 106

Issue


  • 7

Place Of Publication