An investigation of interface bonding of bimetallic foils by combined accumulative roll bonding and asymmetric rolling techniques

Journal Article


Download full-text (Open Access)

Abstract


  • The bond strength in bimetallic materials is an important material characteristic. In this study, 0.1-mm thick bimetallic foils (AA1050/AA6061) were produced using one pass of accumulative roll bonding followed by three passes of asymmetric rolling (AR). The AR passes were carried out at roll speed ratios of 1.0, 1.1, 1.2, 1.3, and 1.4 separately. Finite element simulation was used to model the deformation of the bimetallic foils for the various experimental conditions. Particular attention was focused on the bonding of the interface between AA1050 and AA6061 layers in the simulation. The optimization of the roll speed ratio was obtained for improvement of the bond strength of the interface of AA1050/AA6061 bimetallic foils during AR process. In the simulation, the mean equivalent strain at the interface zone between the AA1050 and AA6061 layers was seen to reach a peak value at a roll speed ratio of about 1.2 to 1.3, which also corresponded to a high quality bond at the interface as observed experimentally.

Publication Date


  • 2014

Citation


  • Yu, H., Tieu, A. Kiet., Lu, C. & Godbole, A. (2014). An investigation of interface bonding of bimetallic foils by combined accumulative roll bonding and asymmetric rolling techniques. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 45A (9), 4038-4045.

Scopus Eid


  • 2-s2.0-84903710617

Ro Full-text Url


  • http://ro.uow.edu.au/cgi/viewcontent.cgi?article=3835&context=eispapers

Ro Metadata Url


  • http://ro.uow.edu.au/eispapers/2826

Has Global Citation Frequency


Number Of Pages


  • 7

Start Page


  • 4038

End Page


  • 4045

Volume


  • 45A

Issue


  • 9

Place Of Publication


  • United States

Abstract


  • The bond strength in bimetallic materials is an important material characteristic. In this study, 0.1-mm thick bimetallic foils (AA1050/AA6061) were produced using one pass of accumulative roll bonding followed by three passes of asymmetric rolling (AR). The AR passes were carried out at roll speed ratios of 1.0, 1.1, 1.2, 1.3, and 1.4 separately. Finite element simulation was used to model the deformation of the bimetallic foils for the various experimental conditions. Particular attention was focused on the bonding of the interface between AA1050 and AA6061 layers in the simulation. The optimization of the roll speed ratio was obtained for improvement of the bond strength of the interface of AA1050/AA6061 bimetallic foils during AR process. In the simulation, the mean equivalent strain at the interface zone between the AA1050 and AA6061 layers was seen to reach a peak value at a roll speed ratio of about 1.2 to 1.3, which also corresponded to a high quality bond at the interface as observed experimentally.

Publication Date


  • 2014

Citation


  • Yu, H., Tieu, A. Kiet., Lu, C. & Godbole, A. (2014). An investigation of interface bonding of bimetallic foils by combined accumulative roll bonding and asymmetric rolling techniques. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 45A (9), 4038-4045.

Scopus Eid


  • 2-s2.0-84903710617

Ro Full-text Url


  • http://ro.uow.edu.au/cgi/viewcontent.cgi?article=3835&context=eispapers

Ro Metadata Url


  • http://ro.uow.edu.au/eispapers/2826

Has Global Citation Frequency


Number Of Pages


  • 7

Start Page


  • 4038

End Page


  • 4045

Volume


  • 45A

Issue


  • 9

Place Of Publication


  • United States