YBa2Cu3O7−δ (YBCO) coated conductors have been fabricated on CeO2/YSZ/Y2O3 buffered Ni-5at%W tapes by pulsed laser deposition (PLD) using the reel-to-reel process. A multi-coating process for YBCO film was employed, and single and multi-coating methods for YBCO films are compared. X-ray diffraction texture measurements showed good in-plane and out-of-plane crystalline orientations for the YBCO films. Magnetic measurements were carried out on the samples, and the critical current density as a function of the magnetic field was investigated. The results showed that the superconducting properties of YBCO films fabricated by the multi-coating process were better than those prepared by the single coating process.