Significant improvement of Jc in MgB2 bulk superconductor using ball-milled high-purity crystalline boron

Journal Article


Abstract


  • The particle size, purity and form of the starting boron powders play an important role in the superconducting properties of MgB2. In this paper high-purity (99.999%) boron powders with crystalline phase that were processed by ball milling have been used as the precursor powders. It was observed that the critical current density (Jc) value was 9.1 x 103 A cm-2 at 5 K and 8 T, which is two times higher than for a sample with ball-milled amorphous boron powders, and a factor of 40 higher than a sample made from as-supplied amorphous boron powders. Significant Jc improvement at high fields is attributed to the Hc2 enhancement caused by the increased disorder.

Publication Date


  • 2008

Citation


  • Zhang, Y., Xu, X., Zhao, Y., Kim, J., Lu, C., Zhou, S. & Dou, S. Xue. (2008). Significant improvement of Jc in MgB2 bulk superconductor using ball-milled high-purity crystalline boron. Superconductor Science and Technology, 21 (11), 115004-(6pages).

Scopus Eid


  • 2-s2.0-58249118164

Ro Metadata Url


  • http://ro.uow.edu.au/engpapers/1117

Has Global Citation Frequency


Start Page


  • 115004

End Page


  • (6pages)

Volume


  • 21

Issue


  • 11

Abstract


  • The particle size, purity and form of the starting boron powders play an important role in the superconducting properties of MgB2. In this paper high-purity (99.999%) boron powders with crystalline phase that were processed by ball milling have been used as the precursor powders. It was observed that the critical current density (Jc) value was 9.1 x 103 A cm-2 at 5 K and 8 T, which is two times higher than for a sample with ball-milled amorphous boron powders, and a factor of 40 higher than a sample made from as-supplied amorphous boron powders. Significant Jc improvement at high fields is attributed to the Hc2 enhancement caused by the increased disorder.

Publication Date


  • 2008

Citation


  • Zhang, Y., Xu, X., Zhao, Y., Kim, J., Lu, C., Zhou, S. & Dou, S. Xue. (2008). Significant improvement of Jc in MgB2 bulk superconductor using ball-milled high-purity crystalline boron. Superconductor Science and Technology, 21 (11), 115004-(6pages).

Scopus Eid


  • 2-s2.0-58249118164

Ro Metadata Url


  • http://ro.uow.edu.au/engpapers/1117

Has Global Citation Frequency


Start Page


  • 115004

End Page


  • (6pages)

Volume


  • 21

Issue


  • 11