Uncovering the mechanism of dislocation interaction with nanoscale (<4 nm) interphase precipitates in microalloyed ferritic steels

Journal Article


Abstract


  • © 2020, © 2020 The Author(s). Published by Informa UK Limited, trading as Taylor & Francis Group. Nanoscale interphase precipitation in microalloyed ferritic steels provides a remarkable (200–400 MPa) strengthening increment, however its origin is unclear. Scanning transmission electron microscopy revealed step formation at the matrix/precipitate interface after both macroscopic uniaxial tension and nanopillar compression testing. Supported by Density Functional Theory modelling, dislocation shearing of nano-sized (<4 nm) VC precipitates was identified as a strengthening mechanism. The findings suggest the operation of an unusual {001}<110> slip–system in the VC nanoparticles. IMPACT STATEMENT: Shearing of VC nanoparticles by dislocations on a non-traditional slip–system was identified as a strengthening mechanism for steels with <4 nm nanoparticles.

Publication Date


  • 2020

Citation


  • Pereloma, E., Cortie, D., Singh, N., Casillas-Garcia, G. & Niessen, F. (2020). Uncovering the mechanism of dislocation interaction with nanoscale (<4 nm) interphase precipitates in microalloyed ferritic steels. Materials Research Letters, 8 (9), 341-347.

Scopus Eid


  • 2-s2.0-85085167902

Number Of Pages


  • 6

Start Page


  • 341

End Page


  • 347

Volume


  • 8

Issue


  • 9

Place Of Publication


  • United States

Abstract


  • © 2020, © 2020 The Author(s). Published by Informa UK Limited, trading as Taylor & Francis Group. Nanoscale interphase precipitation in microalloyed ferritic steels provides a remarkable (200–400 MPa) strengthening increment, however its origin is unclear. Scanning transmission electron microscopy revealed step formation at the matrix/precipitate interface after both macroscopic uniaxial tension and nanopillar compression testing. Supported by Density Functional Theory modelling, dislocation shearing of nano-sized (<4 nm) VC precipitates was identified as a strengthening mechanism. The findings suggest the operation of an unusual {001}<110> slip–system in the VC nanoparticles. IMPACT STATEMENT: Shearing of VC nanoparticles by dislocations on a non-traditional slip–system was identified as a strengthening mechanism for steels with <4 nm nanoparticles.

Publication Date


  • 2020

Citation


  • Pereloma, E., Cortie, D., Singh, N., Casillas-Garcia, G. & Niessen, F. (2020). Uncovering the mechanism of dislocation interaction with nanoscale (<4 nm) interphase precipitates in microalloyed ferritic steels. Materials Research Letters, 8 (9), 341-347.

Scopus Eid


  • 2-s2.0-85085167902

Number Of Pages


  • 6

Start Page


  • 341

End Page


  • 347

Volume


  • 8

Issue


  • 9

Place Of Publication


  • United States