Residual Stress Study of Al/Al Laminates Processed by Accumulative Roll Bonding

Journal Article


Download full-text (Open Access)

Abstract


  • In this work accumulative roll bonding (ARB) was used to combine AA1050 and AA6061 sheets to produce AA1050/AA1050, AA6061/AA6061 and AA1050/AA6061 laminates with ultrafine grained (UFG) structure. Two sheets of starting materials were roll bonded with 200 °C preheating for 180 s before rolling. The through-thickness residual stress distribution of these laminates processed up to two cycles of ARB was determined by neutron diffraction with spatial resolution of 0.2 mm through 1.5 mm thickness. The measurements also required high accuracy of only few MPa since residual stresses in the laminates peaked at only about 15 MPa. The laminates composed of the same material (AA1050/AA1050 and AA6061/AA6061) showed symmetric residual stress profile with tensile stress at the centre of the sheets and compressive stress at the surfaces. The AA1050/AA6061 laminates showed asymmetric distribution with residual tensile stress in the AA1050 layer and compressive stress in the AA6061 layer. A finite element model (FEM) was used to simulate the residual stress distribution and the results were in agreement with the measured results qualitatively.

Publication Date


  • 2016

Citation


  • Su, L., Lu, C., Li, H., Luzin, V., Wang, H. & Tieu, K. (2016). Residual Stress Study of Al/Al Laminates Processed by Accumulative Roll Bonding. Materials Research Proceedings, 2 359-364.

Ro Full-text Url


  • http://ro.uow.edu.au/cgi/viewcontent.cgi?article=7623&context=eispapers

Ro Metadata Url


  • http://ro.uow.edu.au/eispapers/6593

Number Of Pages


  • 5

Start Page


  • 359

End Page


  • 364

Volume


  • 2

Place Of Publication


  • United States

Abstract


  • In this work accumulative roll bonding (ARB) was used to combine AA1050 and AA6061 sheets to produce AA1050/AA1050, AA6061/AA6061 and AA1050/AA6061 laminates with ultrafine grained (UFG) structure. Two sheets of starting materials were roll bonded with 200 °C preheating for 180 s before rolling. The through-thickness residual stress distribution of these laminates processed up to two cycles of ARB was determined by neutron diffraction with spatial resolution of 0.2 mm through 1.5 mm thickness. The measurements also required high accuracy of only few MPa since residual stresses in the laminates peaked at only about 15 MPa. The laminates composed of the same material (AA1050/AA1050 and AA6061/AA6061) showed symmetric residual stress profile with tensile stress at the centre of the sheets and compressive stress at the surfaces. The AA1050/AA6061 laminates showed asymmetric distribution with residual tensile stress in the AA1050 layer and compressive stress in the AA6061 layer. A finite element model (FEM) was used to simulate the residual stress distribution and the results were in agreement with the measured results qualitatively.

Publication Date


  • 2016

Citation


  • Su, L., Lu, C., Li, H., Luzin, V., Wang, H. & Tieu, K. (2016). Residual Stress Study of Al/Al Laminates Processed by Accumulative Roll Bonding. Materials Research Proceedings, 2 359-364.

Ro Full-text Url


  • http://ro.uow.edu.au/cgi/viewcontent.cgi?article=7623&context=eispapers

Ro Metadata Url


  • http://ro.uow.edu.au/eispapers/6593

Number Of Pages


  • 5

Start Page


  • 359

End Page


  • 364

Volume


  • 2

Place Of Publication


  • United States