Microstructural evolution of oxide-dispersion-strengthened Fe-Cr model steels during mechanical milling and subsequent hot pressing

Journal Article


Abstract


  • Oxide-dispersion-strengthened (ODS) ferritic steels of Fe-9Cr-0.3Y 2O3 and Fe-9Cr-0.2Ti-0.3Y2O3 (in mass) incorporating nanoscale oxide particles, were produced by mechanical milling (MM) followed by hot pressing (HP). Microstructural evolution of these two types of ODS steels were structurally characterized at each step of the elaboration processes by means of scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD), and optical microscope. The observations of structure of the mixed powders and the nanoscale oxide particles in both ODS steels after MM indicate that the initial powders, coupled with the original yttria powders, get fractured by severe plastic deformation and ultrafine bcc grains (~20 nm) of the matrix and Y 2O3 nanocrystals with irregular edges are formed during MM. The addition of titanium (Ti) promotes the refinement of bcc grains, Y 2O3 nanocrystals and the formation of amorphous phase of Y2O3 during MM. TEM observations of these two Oxide-dispersion-strengthened (ODS) steels exhibit a very fine structure of micrometer-scale grains in which large number of nanoscale oxide particles are distributed after HP process. The observation of some unreinforced domains without the nanoscale oxide particles indicates that there still exist inhomogeneous areas, although the size of those oxide particles reaches nanoscale. Threshold stress of the HPped Fe-9Cr-0.2Ti-0.3Y2O 3 steel with the relatively homogeneous dispersion was carefully evaluated on the basis of higher magnified images of the nanoscale oxide particles. Different values of threshold stress were obtained due to the various dispersions of the nanoscale oxide particles within different areas. That may be the reason why the threshold stress cannot be clearly obtained by the results of creep tests. © 2012 Springer Science+Business Media New York.

UOW Authors


  •   Ma, Zongqing (external author)
  •   Yu, Liming (external author)
  •   Dai, Lei (external author)
  •   Dong, Zhizhong (external author)
  •   Liu, Yongchang (external author)

Publication Date


  • 2013

Citation


  • Dai, L., Liu, Y., Ma, Z., Dong, Z. & Yu, L. (2013). Microstructural evolution of oxide-dispersion-strengthened Fe-Cr model steels during mechanical milling and subsequent hot pressing. Journal of Materials Science, 48 (4), 1826-1836.

Scopus Eid


  • 2-s2.0-84871789739

Ro Metadata Url


  • http://ro.uow.edu.au/aiimpapers/1955

Has Global Citation Frequency


Number Of Pages


  • 10

Start Page


  • 1826

End Page


  • 1836

Volume


  • 48

Issue


  • 4

Abstract


  • Oxide-dispersion-strengthened (ODS) ferritic steels of Fe-9Cr-0.3Y 2O3 and Fe-9Cr-0.2Ti-0.3Y2O3 (in mass) incorporating nanoscale oxide particles, were produced by mechanical milling (MM) followed by hot pressing (HP). Microstructural evolution of these two types of ODS steels were structurally characterized at each step of the elaboration processes by means of scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD), and optical microscope. The observations of structure of the mixed powders and the nanoscale oxide particles in both ODS steels after MM indicate that the initial powders, coupled with the original yttria powders, get fractured by severe plastic deformation and ultrafine bcc grains (~20 nm) of the matrix and Y 2O3 nanocrystals with irregular edges are formed during MM. The addition of titanium (Ti) promotes the refinement of bcc grains, Y 2O3 nanocrystals and the formation of amorphous phase of Y2O3 during MM. TEM observations of these two Oxide-dispersion-strengthened (ODS) steels exhibit a very fine structure of micrometer-scale grains in which large number of nanoscale oxide particles are distributed after HP process. The observation of some unreinforced domains without the nanoscale oxide particles indicates that there still exist inhomogeneous areas, although the size of those oxide particles reaches nanoscale. Threshold stress of the HPped Fe-9Cr-0.2Ti-0.3Y2O 3 steel with the relatively homogeneous dispersion was carefully evaluated on the basis of higher magnified images of the nanoscale oxide particles. Different values of threshold stress were obtained due to the various dispersions of the nanoscale oxide particles within different areas. That may be the reason why the threshold stress cannot be clearly obtained by the results of creep tests. © 2012 Springer Science+Business Media New York.

UOW Authors


  •   Ma, Zongqing (external author)
  •   Yu, Liming (external author)
  •   Dai, Lei (external author)
  •   Dong, Zhizhong (external author)
  •   Liu, Yongchang (external author)

Publication Date


  • 2013

Citation


  • Dai, L., Liu, Y., Ma, Z., Dong, Z. & Yu, L. (2013). Microstructural evolution of oxide-dispersion-strengthened Fe-Cr model steels during mechanical milling and subsequent hot pressing. Journal of Materials Science, 48 (4), 1826-1836.

Scopus Eid


  • 2-s2.0-84871789739

Ro Metadata Url


  • http://ro.uow.edu.au/aiimpapers/1955

Has Global Citation Frequency


Number Of Pages


  • 10

Start Page


  • 1826

End Page


  • 1836

Volume


  • 48

Issue


  • 4